Structural effects on the magnetic and transport properties of perovskiteA1−xAx′MnO3(x=0.25,0.30)
The evolution of the structural properties of ${A}_{1\ensuremath{-}x}{A}_{x}^{\ensuremath{'}}{\mathrm{MnO}}_{3}$ was determined as a function of temperature, average $A$-site radius $〈{r}_{A}〉,$ and applied pressure for the ``optimal'' doping range $x=0.25,$ 0.30, by using high-resolution neutron powder diffraction. The metal-insulator transition, which can be induced both as a function of temperature and of $〈{r}_{A}〉,$ was found to be accompanied by significant structural changes. Both the paramagnetic charge-localized phase, which exists at high temperatures for all values of $〈{r}_{A}〉,$ and the spin-canted ferromagnetic charge-ordered phase, which is found at low temperatures for low values of $〈{r}_{A}〉,$ are characterized by large metric distortions of the ${\mathrm{MnO}}_{6}$ octahedra. These structural distortions are mainly incoherent with respect to the space-group symmetry, with a significant coherent component only at low $〈{r}_{A}〉.$ These distortions decrease abruptly at the transition into the ferromagnetic metal phase. These observations are consistent with the hypothesis that, in the insulating phases, lattice distortions of the Jahn-Teller type, in addition to spin scattering, provide a charge-localization mechanism. The evolution of the average structural parameters indicates that the variation of the electronic bandwidth is the driving force for the evolution of the insulator-to-metal transition at ${T}_{C}$ as a function of ``chemical'' and applied pressure.